What is Hot Forging

Hot forging entails the heating of a workpiece to about 75% of its melting temperature. This allows for the flow of stress and energy required to form the metal to lower, effectively increasing the rate of production (or strain rate). Hot forging aids in making the metal easier to shape as well as less likely to fracture.

Average temperatures for hot forging includes:

Aluminum (Al) Alloys - 360° (680°F) to 520°C (968°F)
Copper (Cu) Alloys - 700°C (1 292°F) - 800°C (1 472°F)
Steel – up to 1 150°C (2 102°F)

Iron, along with its alloys, are almost always hot forged for two main reasons:

If work hardening progresses, hard materials (such as steel and iron) will become more difficult to work with, and
It is a more economical option to hot forge metals such as steel and then follows with heat treatment processes as metals such as steel can be strengthened through other processes (and not necessarily just cold working processes).

While other materials need to be strengthened through the forging process itself, materials such as most of the titanium and aluminum alloys, can be hot forged and then hardened.

During hot forging processes, the temperature reaches above the recrystallization point of the metal being formed. Being a process in which metals are plastically deformed above their recrystallization temperature, these high temperatures are required in order to avoid strain hardening during deformation.

This process usually involves heating the metal (to the above its recrystallization point) after which it is smashed into a die – depending on the requirements, this die can also be heated. Because the metal is hot, it ‘moves around’ easily and allows manufacturers to create more elaborate shapes than with cold forging.

With superalloys (which have low forge ability), processes such as isothermal forging – where deformation takes place within a controlled atmosphere - is used in order to avoid oxidation.

Isothermal forging, also known as hot die forging, is a hot working process which entails the workpiece is maintained at its maximum elevated temperature throughout the entire forming process.

Maintaining this temperature is done by heating the die – this will be at the temperature of, or slightly lower than the elevated temperature of the workpiece. Forces exerted by this die forms the workpiece and, because the die is also at an elevated temperature, cooling of the workpiece between the mold work interface is eliminated. This, in turn, results in an improvement of the metal’s (workpiece’s) flow characteristics.

Note here that isothermal forging can also be performed in a vacuum.

Hot Working Dies
The dies used in hot forging undergo severe thermal cycle and mechanical loading. This, in turn, affects the life of the die, as the die is open to:

Gross Cracking
Plastic Deformation
Thermal Fatigue Cracking

Depending on the type of forging operation used, the material and the size of the part to be formed, to name but a few examples, forging dies are required to have the following properties and characteristics:

The Benefits of Hot Forging
Commonly used for the type of parts that have an influence in technical applications, hot forging is also a recommended process for deformation of metals that feature high formability ratios.

A sufficient hardness as well as the ability to retain this hardness at elevated temperatures.
A sufficient hardenability as well as a resistance to fatigue.
Good ductility and toughness in all directions at both elevated and low temperatures.
Enhanced levels of both hot hardness and hot tensile strength.

The advantages of hot forging include:

An increased ductility.
Because of the decrease in yield strength, it takes less energy (or force) to work with the material.
During hot forging and subsequent deformation, pores can reduce (in size) or close completely.
Because the elevated temperatures increase diffusion it is possible, in turn, to reduce or remove chemical inhomogeneity.
In hot forging steel, the weak and ductile FCC (face-centered cubic) austenite is deformed instead of the strong BCC (body-centered cubic) ferrite – which would deform at lower forging temperatures.

The Disadvantages of Hot Forging
Hot-working, as all metal forming processes, also has a set of disadvantages. These disadvantages include:

The result of a less precise tolerance caused by warping and thermal contraction. This is caused in instances where uneven cooling is present.
There is the possibility that the grain structure may vary throughout the metal.
With hot working, there is also the possibility of an undesirable reaction between the metal being forged and the surrounding atmosphere.

Deshengrui Machinery is a professional CNC manufacturing and sheet metal fabrication company, including CNC machining services, CNC turning service, CNC milling services, CNC drilling services, laser cutting services, stamping services, die casting service, iron casting service and steel forging service.